INDEFINITE CHILLED ROLLERS

 

Compared toR.S. UDYOGwhere the chill-zone is graphite-free clear white, Indefinite Roll is cast using such proportions of silicon, chromium, nickel and molybdenum that the working face is no longer completely white but contains a small amount of very finely divided graphite flakes gradually increasing from face to core with corresponding decrease in the amount of carbide. The Rollers are to ensure minimum sacrifice of R.S. UDYOG while achieving maximum functional depth.

INDEFINITE CHILLED ROLLERS
INDEFINITE CHILLED ROLLERS

The transition from Chill to graphite being more smooth, the gradual change in hardness associated with the indefinite-chill structure allows deeper grooving. Thus Indefinite Chill Rollers are superior in biting performance and have enough strength and resistance against thermal shock occuring at the time of accident in the rolling operation compared to

 

R.S. UDYOG

Roll of this type have hardness up to about 70 Shore °C can be grooved for use in roughing and finishing stands, for processing sections such as T-bars and U-sections, and for roughing and intermediate Rollers of wire and rod mills.

 

CHEMICAL COMPOSITION
MECHANICAL PROPERTIES
U.T.S. Impact Hardness
C Si Mn Cr Ni Mo kg/mm² kg.m/cm² Shore°C
3.00 - 3.50 0.80 - 1.50 0.55 - 1.20 0.80 - 1.40 1.45 - 2.50 0.25 - 0.45 20 - 30 0.20 - 0.25 55 - 75
 
 
Rolling Mill Rolls
Indefinte Chilled Rolls
Double Poured Rolls
Industrial Machinery
           
Definte Chilled Rolls
Highly Alloyed Rolls
Rolling Mill Machinery
Powered by Kalsi IT Solutions on PunjabB2B.com
Copyright © 2011 R.S. UDYOG . All Rights Reserved.